BASF Ultrafuse PLA

In stock (6 items available)

Ultrafuse® PLA (previously Innofil3D PLA,  different name, same high-quality product!) is Poly-Lactic-Acid, a biodegradable polymer with a low melting point.
It is an easy material to print with and Ultrafuse PLA gives a smooth printing result.
This most used 3D printing material is available in a wide range of RAL colors and translucent variants.  

  • $29.99
Qty:  
  • SKU
    50712112

Ultrafuse® PLA (previously Innofil3D PLA,  different name, same high-quality product!) is Poly-Lactic-Acid, a biodegradable polymer with a low melting point.
It is an easy material to print with and Ultrafuse PLA gives a smooth printing result.
This most used 3D printing material is available in a wide range of RAL colors and translucent variants.

When properly cooled, PLA has a higher maximum printing speed, lower layer heights, and sharper printed corners.

Combining this with low warping of the print makes it a popular plastic for makers, prosumers and schools.

Quality

We select the best raw materials available from renowned suppliers.

Dedicated people, highest standards.

Production on our state-of-the-art computer-controlled machinery guarantees a truly consistent filament, also between colors and batches.

It will perform as expected, every time.

All our products are 100% traceable to the source.

Tips & Tricks

Curious about our settings with Ultrafuse PLA?

We are printing with the following settings;

  • Print temperature 210-220 degrees
  • Heated bed at 60 degrees
  • Print speed at 30-80 mm/s

Reference Links and Documents

Technical Data Sheet - Download
Safety Data Sheet - Download

  • Brand
    BASF
  • Color
    Pearl White, Gold, Bronze, Army Green, Chocolate Brown, Apricot Skin, Dark Green TR, Ice Blue TR, Sky Blue, White
  • Size
    750g
  • Diameter
    1.75 mm, 2.85 mm
  • Manufacturer
    BASF
  • Brand
    BASF
  • Nozzle Diameter
    ≥ 0.4 mm
  • Printed Part Density
    1248 kg/m3 / 77.9 lb/ft3
  • Drying recommendations
    PLA is in a printable condition, drying is not necessary
  • Print Speed
    40 - 80 mm/s
  • Nozzle Temperature
    210 – 230 °C / 410 – 446 °F
  • Build Chamber Temperature
    -
  • Bed Temperature
    50 – 70 °C / 122 – 158 °F
  • Bed material
    Glass
  • Thermal Properties
    HDT at 1.8 MPa 55 °C / 131 °F
    HDT at 0.45 MPa 65 °C / 149 °F
    Glass Transition Temperature 61 °C / 142 °F
    Melting Temperature 151 °C / 304 °F
    Melt Volume Rate 21.2 cm3/10 min / 1.29 in3/10 min (220 °C, 5 kg)